Optimize Steel Production with Cored Wire and Copper Tube
CaSi CORED WIRE;
Ca:28-32%, Si:58-62%, Al:2%max, C:1.0%max
Dia: 13mm+/-0.5mm Thickness:0.4+/-0.05mm
Filling rate:230+/-10g/m,1135kg/coil+/-10%
Steel weight:165+/-10g/m,765kg/coil+/-10%
Wire weight:395+/-10g/m,1900kg/coil+/-10%
Wire length: 4935m+/-10% Coil ID: 600mm Coil OD: 1100mm Height: 1100mm
CaFe CORED WIRE
Ca:28-32%, Fe:68-72%
Dia: 13mm+/-0.5mm
Thickness:0.4+/-0.05mm
Filling rate:260+/-10g/m,1250kg/coil+/-10%
Steel weight:165+/-10g/m,750kg/coil+/-10%
Wire weight:425+/-10g/m,2000kg/coil+/-10%
Wire length: 4820m+/-10%
Coil ID: 600mm Coil OD: 1100mm Height: 1100mm
PURE Ca CORED WIRE
Ca:98.5%min
Dia: 9mm+/-0.5mm
Thickness:0.5+/-0.05mm
Filling rate: 70+/-5g/m
Wire weight:2000kg/coil+/-10%
Wire length: 9090m+/-10%
Coil ID: 600mm Coil OD: 1100mm Height: 1100
WATER COOLED COPPER CABLE FOR EAF&LF
GRAPHITE ELECTRODE FOR EAF&LF
The Graphite electrodes are produced through calcined material under high pressure in vacuum impregnation and then Graphitized at Graphitization Furnace; finally they are machined.The electrodes are supplied 100-700mm diameter with specification RP(Regular Power), HP and UHP.
High Power grade is for foundry operations, for the ladle furnace and occasionally for the electric arc furnace operations, if the furnace parameters are suitable. Ultra High Power grade is suitable for the electric arc furnace (EAF) operations and the ladle furnace operations with heavy current loads.
COPPER TUBE FOR CCM
ESR FLUX
TOOL STEELS
Cold Work Tool Steel
Hot Work Tool Steel
High Speed Steel
Plastic Mold Steel
CONSTRUCTION STEEL
ALL KINDS OF PROFILES